MAG Material / Flux-Cored Wire for Soft Steel to 550 MPa Grade Steel MX-100/MX-Z100

Suitable for protruding and fillet welding (downward and lateral). Capable of high-efficiency welding construction. Slag volume is about the same as that of solid wire.

Part Number

Once your search is narrowed to one product,
the corresponding part number is displayed here.

MX-Z100-1.2-20

Part Numbers

Data to be displayed: 30; 45; 60

Part Number
MX-Z100-1.2-20

Part Number	Standard Unit Price	Minimum order quantity	Volume Discount	Standard Shipping Days ?	Wire Diameter (mm)	Current range, lower (A)	Lateral horizontal fillet
	175.88 €	1		8 Days	1.2	200～350	200~300

Basic information

Product Type	Welding wire	JIS Standard	Z3313 T 49J 0 T15-0 C A-U (Previously YFW-C50DM)	AWS Standard	A5.20 E70T-1C Applicable
Compatible Material Type	Characterized by Low Spatter with High Welding	Amount Of Content	1 Box (20 kg)	Mass(g)	20000
Application and Usage Characteristic	Butt-jointing or fillet welding of steel frames, industrial machines, construction machines, etc. Solid wire welding speed can be increased by 10 to 30%. In addition, spatter generation is halved and removal work is reduced. Amount of slag is similarly small, and multi-layer welding is possible.	Main Points of Work	General constant voltage power supply can be used. With a diameter of 1.6 mm or more, the high capacity power supply (ex: 600 A, low standard 100% specifications) and corresponding torch are required.	Chemical Composition of Deposited Metal C(%)	0.06
Chemical Composition of Deposited Metal Si(%)	0.62	Chemical Composition of Deposited Metal Mn(%)	1.35	Chemical Composition of Deposited Metal P(%)	0.014
Chemical Composition of Deposited Metal S(%)	0.011	Mechanical Properties of Weld Metal Proof Stress MPa	510	Mechanical Properties of Weld Metal Proof Stress, Tensile Strength MPa	580
Mechanical Properties of Weld Metal Proof Stress, Elongation(%)	27	Mechanical Properties of Weld Metal Proof Stress, Absorption Energy(J)	88