Coated Rod for Soft Steel to 550 MPa Grade Steel B-10【1-4 Pieces Per Package】

It is used for the welding of general structures on vehicles, and in construction. Suitable for protruding and fillet welding of thin sheets around 20 mm or less. Provides stable slag covering for flat welding and beautiful, glossy beads. Even greater weld permeation in high titanium oxides and lime titania which is suitable for welded joints and even thin plates that require ample welding permeation.

Part Number

Once your search is narrowed to one product,
the corresponding part number is displayed here.

Products homepage

Data to be displayed: 30; 45; 60

Part Number
B-10-2.6-5
B-10-2.6-20
B-10-3.2-5
B-10-3.2-20
B-10-4-5
B-10-4-20

Standard Unit Price	Number of pc(s). included in pkg.	Minimum order quantity	Standard Shipping Days ?	Pole diameter (mm)	Pole length (mm)	Current range, lower (A)	Current range, vertical position, elevating, upper	Amount Of Content	Mass (g)
66.04 €		1	4 Days	2.6	350	50~85	40–70	1 Case (5 kg)	5000
179.00 €	4 Pieces Per Package	1 pack	7 Days	2.6	350	50~85	40–70	1 Box (5 kg x 4 Cases)	20000
61.47 €		1	5 Days	3.2	350	80～130	60~110	1 Case (5 kg)	5000
164.09 €	4 Pieces Per Package	1 pack	7 Days	3.2	350	80～130	60~110	1 Box (5 kg x 4 Cases)	20000
59.23 €		1	5 Days	4	400	120～180	100~150	1 Case (5 kg)	5000
158.04 €	4 Pieces Per Package	1 pack	7 Days	4	400	120～180	100~150	1 Box (5 kg x 4 Cases)	20000

Basic information

Product Type	Welding rod	JIS Standard	Z3211 E4319	AWS Standard	A5.1 E6019 Applicable
Compatible Material Type	For general structures	Application and Usage Characteristic	For welding general structures such as vehicles and buildings. It's suitable for butt-jointing and fillet welding of thin plate up to about 20 mm. The slag covering in the downward direction is stable, so a glossy, beautiful bead is obtained. The weld penetration is higher than with high-titanium oxide types and lime titania types, so it is suitable for welded joints that need sufficient weld penetration, even thin plate.	Main Points of Work	Excessive current reduces X-ray performance and is the reason for degradation of workability. Hence, use the appropriate current range. Due to excessive absorption of moisture, besides deterioration of workability, pits may also occur. Hence, dehydrate at 70 to 100°C for 30 to 60 minutes. Due to excessive drying (for long period or high temperature), the penetration decreases, X-ray performance deteriorates and causes burning of the bar, even though there is no apparent change in quality. For medium and thick welding, adopt appropriate preheating / inter-path temperature.
Chemical Composition of Deposited Metal C(%)	0.10	Chemical Composition of Deposited Metal Si(%)	0.09	Chemical Composition of Deposited Metal Mn(%)	0.39
Chemical Composition of Deposited Metal P(%)	0.016	Chemical Composition of Deposited Metal S(%)	0.008	Identification Color, Rod End Color	Green
Identification Color, Secondary Color	NA	Mechanical Properties of Weld Metal Proof Stress MPa	400	Mechanical Properties of Weld Metal Proof Stress, Tensile Strength MPa	450
Mechanical Properties of Weld Metal Proof Stress, Elongation(%)	26	Mechanical Properties of Weld Metal Proof Stress, Absorption Energy(J)	95